Staurolite
Caucia F, Callegari A, Oberti R, Ungaretti L, Hawthorne F C
The Canadian Mineralogist 32 (1994) 477-489
Structural aspects of oxidation-dehydrogenation in staurolite
Sample: T = 25 C
_database_code_amcsd 0005371
7.864 16.619 5.659 90 90.17 90 C2/m
atom       x      y      z occ Biso
SiT1  .13413 .16602 .24851 .95  .29
AlT1  .13413 .16602 .24851 .05  .29
FeT2  .39198      0 .24777 .69 1.17
ZnT2  .39198      0 .24777 .01 1.17
MgT2  .39198      0 .24777 .10 1.17
AlT2  .39198      0 .24777 .13 1.17
AlM1A     .5 .17527      0 .97  .36
MgM1A     .5 .17527      0 .02  .36
FeM1A     .5 .17527      0 .01  .36
AlM1B     .5 .17510     .5 .97  .36
MgM1B     .5 .17510     .5 .02  .36
FeM1B     .5 .17510     .5 .01  .36
AlM2  .26336 .41067 .25170 .97  .47
MgM2  .26336 .41067 .25170 .01  .47
FeM2  .26336 .41067 .25170 .02  .47
AlM3A      0      0      0 .82  .43
MgM3A      0      0      0 .04  .43
FeM3A      0      0      0 .06  .43
AlM3B      0      0     .5 .82  .42
MgM3B      0      0     .5 .04  .42
FeM3B      0      0     .5 .06  .42
FeM4A     .5      0      0 .04  .75
FeM4B     .5      0     .5 .04  .80
O1A   .23340      0 .96302  .5  .67
OH1A  .23340      0 .96302  .5  .67
O1B   .23618      0 .53372  .5  .72
OH1B  .23618      0 .53372  .5  .72
O2A   .25552 .16153 .01537      .41
O2B   .25437 .16126 .48387      .43
O3    .00177 .08894 .24523      .63
O4    .02154 .24918 .24963      .42
O5    .52700 .10039 .24952      .40