Staurolite
Caucia F, Callegari A, Oberti R, Ungaretti L, Hawthorne F C
The Canadian Mineralogist 32 (1994) 477-489
Structural aspects of oxidation-dehydrogenation in staurolite
Sample: T = 600 C
_database_code_amcsd 0005374
7.865 16.612 5.648 90 90.04 90 C2/m
atom       x      y      z occ Biso
SiT1  .13432 .16631 .24962 .95  .32
AlT1  .13432 .16631 .24962 .05  .32
FeT2  .38949      0 .24965 .55 1.15
AlT2  .38949      0 .24965 .15 1.15
MgT2  .38949      0 .24965 .09 1.15
ZnT2  .38949      0 .24965 .01 1.15
FeT3  .12856      0 .25020 .04  .39
AlT3  .12856      0 .25020 .10  .39
AlM1A     .5 .17480      0 .97  .39
MgM1A     .5 .17480      0 .01  .39
FeM1A     .5 .17480      0 .02  .39
AlM1B     .5 .17481     .5 .97  .39
MgM1B     .5 .17481     .5 .01  .39
FeM1B     .5 .17481     .5 .02  .39
AlM2  .26355 .41100 .25035 .94  .53
FeM2  .26355 .41100 .25035 .06  .53
AlM3A      0      0      0 .68  .45
MgM3A      0      0      0 .04  .45
FeM3A      0      0      0 .06  .45
AlM3B      0      0     .5 .68  .44
MgM3B      0      0     .5 .04  .44
FeM3B      0      0     .5 .06  .44
FeM4A     .5      0      0 .05 1.00
MgM4A     .5      0      0 .04 1.00
FeM4B     .5      0     .5 .05 1.04
MgM4B     .5      0     .5 .04 1.04
O1A   .23536      0 .96507  .5  .74
O1B   .23581      0 .53402  .5  .77
O2A   .25517 .16153 .01533  .5  .44
O2B   .25482 .16153 .48456  .5  .44
O3    .00196 .08917 .24895      .64
O4    .02150 .24930 .24974      .43
O5    .52677 .09984 .24991      .43