Natrozippeite
Burns P C, Deely K M, Hayden L A
The Canadian Mineralogist 41 (2003) 687-706
The crystal chemistry of the zippeite group
Sample : Sodium-zippeite
_database_code_amcsd 0005848
17.6425 14.6272 17.6922 90 104.461 90 P2_1/n
atom         x      y      z Uiso
U(1)     .3384  .2323  .8377 .010
U(2)     .2603  .2250  .0096 .011
U(3)     .5845  .2563  .8347 .010
U(4)     .4991  .2649  .0090 .012
U(5)     .8257  .2186  .8326 .013
U(6)     .7569  .2168  .0078 .011
U(7)     .9965  .2462  .0091 .011
U(8)     .0942  .2516  .8329 .011
S(1)     .9213  .2450  .1710 .008
S(2)     .6668  .2487  .6713 .015
S(3)     .1714  .2458  .6728 .013
S(4)     .4235  .2604  .1748 .018
Na(1)    .1795  .0228  .6734 .036
Na(2)    .9192  .0301  .1916 .032
Na(3)    .6705  .0145  .6745 .048
Na(4)    .2360  .5004  .9907 .046
Na(5)    .5668 -.0291  .8133 .043
O(1)     .7185  .2377  .8768 .013
O(2)     .2214  .2414  .8779 .015
O(3)     .5954  .3747  .8692 .018
O(4)     .8686  .2377  .9643 .022
O(5)     .8847  .3117  .2154 .020
O(6)     .2309  .1871  .7202 .019
O(7)     .2080  .3149  .6278 .018
O(8)     .1337  .3037  .7213 .018
O(9)     .8624  .1848  .1255 .018
O(10)    .4729  .2450  .8799 .013
O(11)    .3696  .2623  .9683 .017
O(12)    .7085  .3147  .6280 .019
O(13)    .3322  .3496  .8121 .021
O(14)    .7216  .1851  .7140 .018
O(15)    .0930  .3690  .8667 .019
O(16)    .3818  .3255  .2160 .018
O(17)    .4992  .1524  .0407 .020
O(18)    .6358  .3083  .7252 .021
O(19)    .4799  .2056  .2320 .022
O(20)    .9539  .3039  .1201 .018
O(21)    .9804  .1908  .2249 .020
O(22)    .3661  .2008  .1288 .020
O(23)    .1148  .1929  .6148 .019
O(24)    .7546  .0975  .9966 .019
O(25)    .4589  .3169  .1254 .027
O(26)    .9956  .3654  .9767 .022
O(27)    .5049  .3870  .9916 .015
O(28)    .2428  .3411  .0265 .017
O(29)    .6054  .2019  .6121 .024
O(30)    .2683  .1061  .9993 .020
O(31)    .0030  .1325  .0427 .027
O(32)    .8352  .3363  .8148 .024
O(33)    .3437  .1129  .8528 .023
O(34)    .5723  .1437  .7954 .024
O(35)    .8250  .0989  .8445 .021
O(36)    .7528  .3328  .0271 .030
O(37)    .0887  .1392  .7969 .016
OH(1)    .6162  .2071  .9681 .012
OH(2)    .1173  .2052  .9675 .010
OH(3)    .9711  .2025  .8742 .015
Wat(1)   .7841  .0122  .1888 .031
Wat(2)   .0414  .0053  .6702 .027
Wat(3)   .6972 -.0229  .8079 .036
Wat(4)   .5305  .0063  .6683 .031
Wat(5)   .0480  .0022  .1788 .051
Wat(6)   .1412 -.0129  .5355 .038
Wat(7)   .1204  .5020  .0309 .034
Wat(8)   .5990  .0173  .9523 .042
Wat(9)   .3089  .0227  .6512 .033
Wat(10)  .8885 -.0189  .0471 .033
Wat(11)  .7943  .0069  .6457 .041
Wat(12)  .4353 -.0215  .8036 .043