Mordenite
Martucci A, Sacerdoti M, Cruciani G, Dalconi C
European Journal of Mineralogy 15 (2003) 485-493
In situ time resolved synchrotron powder diffraction study of mordenite
Sample: T = 25 C
_database_code_amcsd 0006995
18.120 20.494 7.531 90 90 90 Cmcm
atom    x    y    z   occ Uiso
NaA     0   .5    0  .775 .033
WatA    0   .5    0  .225 .033
KB      0 .579  .25  .035 .140
WatB    0 .579  .25  .485 .140
CaC  .444 .215  .25  .118 .150
MgC  .444 .215  .25 .0055 .150
SrC  .444 .215  .25 .0005 .150
WatD   .5 .335  .25  .716 .140
WatE .627 .481  .25  .952 .110
CaF    .5 .478  .25  .236 .043
MgF    .5 .478  .25  .011 .043
SrF    .5 .478  .25  .001 .043
WatF   .5 .478  .25  .173 .043
WatG   .5 .398 .487  .793 .096
WatH .111    0    0  .294 .015
WatJ    0 .060 .064  .610 .098
SiT1 .303 .072 .037 .8444 .011
AlT1 .303 .072 .037 .1542 .011
FeT1 .303 .072 .037 .0006 .011
SiT2 .305 .311 .046 .8444 .011
AlT2 .305 .311 .046 .1542 .011
FeT2 .305 .311 .046 .0006 .011
SiT3 .088 .388  .25 .8444 .011
AlT3 .088 .388  .25 .1542 .011
FeT3 .088 .388  .25 .0006 .011
SiT4 .085 .229  .25 .8444 .011
AlT4 .085 .229  .25 .1542 .011
FeT4 .085 .229  .25 .0006 .011
O1   .118 .414 .443       .024
O2   .121 .191 .422       .024
O3   .231 .117 .990       .024
O4   .095 .308  .25       .024
O5   .163 .193  .75       .024
O6   .179 .422  .75       .024
O7   .235   .5   .5       .024
O8    .25  .25   .5       .024
O9      0 .405  .25       .024
O10     0 .203  .25       .024