Mordenite
Martucci A, Sacerdoti M, Cruciani G, Dalconi C
European Journal of Mineralogy 15 (2003) 485-493
In situ time resolved synchrotron powder diffraction study of mordenite
Sample: T = 200 C
_database_code_amcsd 0006996
18.074 20.446 7.531 90 90 90 Cmcm
atom     x    y    z   occ Uiso
WatA     0   .5    0   .75 .113
WatB     0 .569 .154  .449 .136
CaC'  .410 .116  .25  .023  .08
MgC'  .410 .116  .25  .001  .08
SrC'  .410 .116  .25 .0001  .08
WatC' .410 .116  .25  .096  .08
CaD'    .5 .254 .377  .031  .14
MgD'    .5 .254 .377 .0014  .14
SrD'    .5 .254 .377 .0001  .14
WatD'   .5 .254 .377  .133  .14
WatE  .600 .502  .25  .519 .116
CaF     .5 .407  .25 .3315 .130
MgF     .5 .407  .25 .0031 .130
SrF     .5 .407  .25 .0004 .130
WatF    .5 .407  .25  .141 .130
WatG    .5 .351 .419  .061 .100
WatG'   .5 .351 .419  .061 .100
WatH  .090    0    0  .178 .102
WatJ     0 .103 .003  .501 .101
SiT1  .306 .075 .034 .8444 .048
AlT1  .306 .075 .034 .1542 .048
FeT1  .306 .075 .034 .0006 .048
SiT2  .306 .308 .041 .8444 .048
AlT2  .306 .308 .041 .1542 .048
FeT2  .306 .308 .041 .0006 .048
SiT3  .092 .385  .25 .8444 .048
AlT3  .092 .385  .25 .1542 .048
FeT3  .092 .385  .25 .0006 .048
SiT4  .086 .226  .25 .8444 .048
AlT4  .086 .226  .25 .1542 .048
FeT4  .086 .226  .25 .0006 .048
O1    .122 .414 .443       .062
O2    .124 .187 .416       .062
O3    .237 .126 .986       .062
O4    .090 .308  .25       .062
O5    .158 .201  .75       .062
O6    .185 .423  .75       .062
O7    .234   .5   .5       .062
O8     .25  .25   .5       .062
O9       0 .400  .25       .062
O10      0 .203  .25       .062