Mordenite
Martucci A, Sacerdoti M, Cruciani G, Dalconi C
European Journal of Mineralogy 15 (2003) 485-493
In situ time resolved synchrotron powder diffraction study of mordenite
Sample: T = 450 C
_database_code_amcsd 0006997
18.024 20.386 7.503 90 90 90 Cmcm
atom     x    y     z   occ Uiso
WatA     0   .5     0   .72 .107
WatB     0 .559  .127  .260 .125
WatC' .441 .125   .25  .131 .151
WatD'   .5 .251  .372  .110 .139
WatE  .586 .523   .25  .146 .166
WatG    .5 .313  .434  .150 .130
WatG'   .5 .313  .434  .150 .130
WatJ     0 .075 -.024  .314 .182
SiT1  .299 .073  .035 .8444 .050
AlT1  .299 .073  .035 .1542 .050
FeT1  .299 .073  .035 .0006 .050
SiT2  .308 .306  .038 .8444 .050
AlT2  .308 .306  .038 .1542 .050
FeT2  .308 .306  .038 .0006 .050
SiT3  .088 .387   .25 .8444 .050
AlT3  .088 .387   .25 .1542 .050
FeT3  .088 .387   .25 .0006 .050
SiT4  .087 .227   .25 .8444 .050
AlT4  .087 .227   .25 .1542 .050
FeT4  .087 .227   .25 .0006 .050
O1    .124 .414  .436       .068
O2    .118 .191  .428       .068
O3    .236 .125  .980       .068
O4    .086 .306   .25       .068
O5    .159 .191   .75       .068
O6    .177 .417   .75       .068
O7    .233   .5    .5       .068
O8     .25  .25    .5       .068
O9       0 .409   .25       .068
O10      0 .205   .25       .068