Mordenite
Martucci A, Sacerdoti M, Cruciani G, Dalconi C
European Journal of Mineralogy 15 (2003) 485-493
In situ time resolved synchrotron powder diffraction study of mordenite
Sample: T = 830 C
_database_code_amcsd 0006998
18.029 20.308 7.493 90 90 90 Cmcm
atom     x    y    z   occ Uiso
NaA      0   .5    0  .547 .123
WatA     0   .5    0   .88 .123
WatB     0 .559 .125  .104 .090
WatC' .410 .179  .25  .107 .107
WatD'   .5 .288 .350  .133 .142
SiT1  .303 .073 .038 .8444 .058
AlT1  .303 .073 .038 .1542 .058
FeT1  .303 .073 .038 .0006 .058
SiT2  .308 .309 .039 .8444 .058
AlT2  .308 .309 .039 .1542 .058
FeT2  .308 .309 .039 .0006 .058
SiT3  .089 .387  .25 .8444 .058
AlT3  .089 .387  .25 .1542 .058
FeT3  .089 .387  .25 .0006 .058
SiT4  .084 .227  .25 .8444 .058
AlT4  .084 .227  .25 .1542 .058
FeT4  .084 .227  .25 .0006 .058
O1    .119 .413 .442       .079
O2    .120 .197 .429       .079
O3    .234 .121 .993       .079
O4    .085 .306  .25       .079
O5    .158 .197  .75       .079
O6    .167 .421  .75       .079
O7    .230   .5   .5       .079
O8     .25  .25   .5       .079
O9       0 .411  .25       .079
O10      0 .194  .25       .079