Calcium
      Bernstein B T, Smith J F
      Acta Crystallographica 12 (1959) 419-420
      Coefficients of thermal expansion for face-centered cubic and
      body-centered cubic calcium
      Locality: synthetic
      Sample: at T = 26 C
      _database_code_amcsd 0009227

      CELL PARAMETERS:    5.5884   5.5884   5.5884   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    174.527
      Density (g/cm3):      1.525
      MAX. ABS. INTENSITY / VOLUME**2:      30.83607566    
      RIR:      6.584
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                27.65        100.00        3.2265    1   1   1         8
                32.03         48.97        2.7942    2   0   0         6
                45.93         30.41        1.9758    2   2   0        12
                54.46         32.47        1.6850    3   1   1        24
                57.09          9.02        1.6132    2   2   2         8
                66.98          3.62        1.3971    4   0   0         6
                73.93          9.89        1.2821    3   3   1        24
                76.18          8.85        1.2496    4   2   0        24
                85.03          6.07        1.1407    4   2   2        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.