Westerveldite
      Lyman P S, Prewitt C T
      Acta Crystallographica B40 (1984) 14-20
      Room- and high-pressure crystal chemistry of CoAs and FeAs
      Locality: synthetic
      Note: anisoB's taken from ICSD
      Sample: Pna2_1 refinement, P = .0001 GPa
      _database_code_amcsd 0009796

      CELL PARAMETERS:    5.4401   6.0259   3.3712   90.000   90.000   90.000
      SPACE GROUP: Pna2_1    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    110.513
      Density (g/cm3):      7.858
      MAX. ABS. INTENSITY / VOLUME**2:      98.00901749    
      RIR:      4.061
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                30.38          7.05        2.9421    0   1   1         2
                34.01         47.62        2.6357    1   2   0         4
                34.66        100.00        2.5879    1   1   1         4
                36.23          3.94        2.4792    2   1   0         4
                42.71         15.33        2.1169    2   0   1         2
                43.59         36.81        2.0764    1   2   1         4
                44.89         37.55        2.0190    2   2   0         4
                45.41         76.88        1.9973    2   1   1         4
                48.30         11.15        1.8843    1   3   0         4
                52.71         18.63        1.7364    3   1   0         4
                52.86          3.96        1.7321    2   2   1         4
                53.07         40.36        1.7256    0   3   1         2
                54.43         27.81        1.6856    0   0   2         1
                56.99          5.92        1.6158    2   3   0         4
                59.50          2.82        1.5537    3   2   0         4
                59.92          7.44        1.5437    3   1   1         4
                63.89          3.30        1.4571    2   3   1         4
                64.15          8.27        1.4518    1   4   0         4
                65.76         12.65        1.4200    1   2   2         4
                66.23          1.27        1.4110    3   2   1         4
                67.15          1.19        1.3939    2   1   2         4
                69.06          4.24        1.3600    4   0   0         2
                69.88          1.92        1.3460    3   3   0         4
                70.64          2.30        1.3334    1   4   1         4
                71.06          1.96        1.3267    4   1   0         4
                71.60          1.90        1.3179    2   4   0         4
                73.14         14.73        1.2939    2   2   2         4
                75.36          5.33        1.2613    4   0   1         2
                75.71          4.68        1.2563    1   3   2         4
                77.29          3.27        1.2345    4   1   1         4
                79.20          9.95        1.2095    3   1   2         4
                81.87          4.38        1.1767    1   5   0         4
                82.74          3.70        1.1664    2   3   2         4
                83.00          3.37        1.1634    4   2   1         4
                83.41          1.62        1.1588    3   4   0         4
                84.88          1.91        1.1424    3   2   2         4
                85.58          2.05        1.1348    0   5   1         2
                86.40          3.79        1.1262    4   3   0         4
                87.89          4.62        1.1109    1   5   1         4
                88.98          6.35        1.1000    1   4   2         4
                89.42         16.35        1.0958    3   4   1         4
================================================================================