Magnetite
      Fleet M E
      Acta Crystallographica C40 (1984) 1491-1493
      The structure of magnetite: two annealed natural magnetites,
      Fe3.005O4 and Fe2.96Mg0.04O4
      Note: Sample No.633, Fe3.005, annealed at 1373 K for 7 days
      _database_code_amcsd 0009994

      CELL PARAMETERS:    8.3969   8.3969   8.3969   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    592.048
      Density (g/cm3):      5.194
      MAX. ABS. INTENSITY / VOLUME**2:      92.25799512    
      RIR:      5.783
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.30          7.93        4.8480    1   1   1         8
                30.10         28.13        2.9688    2   2   0        12
                35.46        100.00        2.5318    3   1   1        24
                37.09          8.19        2.4240    2   2   2         8
                43.09         20.17        2.0992    4   0   0         6
                53.46          9.58        1.7140    4   2   2        24
                56.99         24.87        1.6160    5   1   1        24
                56.99          6.37        1.6160    3   3   3         8
                62.58         41.78        1.4844    4   4   0        12
                70.99          3.53        1.3277    6   2   0        24
                74.03          8.77        1.2805    5   3   3        24
                75.03          3.84        1.2659    6   2   2        24
                79.00          2.64        1.2120    4   4   4         8
                86.79          3.90        1.1221    6   4   2        48
                89.69          5.49        1.0932    5   5   3        24
                89.69          8.82        1.0932    7   3   1        48
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.