      Hendricks S B, Kosting P R
      Zeitschrift fur Kristallographie 74 (1930) 511-533
      The crystal structure of Fe2P, Fe2N, Fe3N and FeB
      Locality: synthetic
      _database_code_amcsd 0010502

      CELL PARAMETERS:    4.6680   4.6680   4.3620   90.000   90.000  120.000
      SPACE GROUP: P312      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     82.315
      Density (g/cm3):      7.323
      MAX. ABS. INTENSITY / VOLUME**2:      177.5398065    
      RIR:      7.894
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                30.14          2.02        2.9650    1   0   1         6
                38.57         18.21        2.3340    1   1   0         6
                41.40         23.19        2.1810    0   0   2         2
                44.00         50.00        2.0579    2  -1   1         6
                44.00         50.00        2.0579    1   1   1         6
                57.86          8.32        1.5935    2  -1   2         6
                57.86          8.32        1.5935    1   1   2         6
                69.79         14.88        1.3475    3   0   0         3
                77.32          6.91        1.2341    1   1   3         6
                77.32          6.91        1.2341    2  -1   3         6
                84.52         12.24        1.1464    3   0   2         6
                86.29          1.63        1.1274    2   2   1         6
                86.29          1.63        1.1274   -2  -2   1         6
                89.97          2.18        1.0905    0   0   4         2
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs