Luogufengite
      Garcia-Munoz J L, Romaguera A, Fauth F, Nogues J, Gich M
      Unveiling a new high-temperature ordered magnetic phase in e-Fe2O3
      Chemistry of Materials 29 (2017) 9705-9713
      Note: T = 510 K
      Locality: synthetic
      _database_code_amcsd 0021084

      CELL PARAMETERS:    5.0967   8.7953   9.4770   90.000   90.000   90.000
      SPACE GROUP: Pna2_1    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    424.827
      Density (g/cm3):      4.993
      MAX. ABS. INTENSITY / VOLUME**2:      44.15088412    
      RIR:      2.879
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                13.74          5.65        6.4468    0   1   1         2
                18.73          1.99        4.7385    0   0   2         1
                20.14          1.64        4.4098    1   1   0         4
                22.23          1.20        3.9982    1   1   1         4
                26.78          3.69        3.3296    1   2   0         4
                27.63          7.39        3.2282    1   1   2         4
                27.67         16.33        3.2234    0   2   2         2
                28.41          2.73        3.1413    1   2   1         4
                30.06         31.67        2.9731    0   1   3         2
                31.95          2.05        2.8008    0   3   1         2
                32.88        100.00        2.7243    1   2   2         4
                34.94         14.54        2.5681    1   1   3         4
                35.22         16.02        2.5484    2   0   0         2
                35.32          6.99        2.5413    1   3   0         4
                36.51         12.84        2.4609    2   0   1         2
                36.61         26.28        2.4546    1   3   1         4
                36.72          2.89        2.4477    2   1   0         4
                37.98          5.40        2.3693    0   0   4         1
                39.32          8.70        2.2917    1   2   3         4
                40.18          3.89        2.2444    2   0   2         2
                40.27          9.97        2.2396    1   3   2         4
                41.05          4.37        2.1988    0   4   0         2
                41.53         13.49        2.1747    2   1   2         4
                44.90          3.26        2.0190    1   4   0         4
                45.37          2.61        1.9991    2   2   2         4
                45.48          5.56        1.9946    0   4   2         2
                45.74          2.76        1.9834    2   0   3         2
                45.83          6.64        1.9801    1   3   3         4
                46.96          8.19        1.9348    2   1   3         4
                47.08          1.03        1.9304    1   2   4         4
                47.26          1.24        1.9233    2   3   0         4
                49.05          4.05        1.8574    1   4   2         4
                49.17          2.61        1.8529    0   1   5         2
                50.48          2.74        1.8080    2   2   3         4
                52.55          1.25        1.7414    1   1   5         4
                52.76         10.10        1.7352    2   0   4         2
                52.83          6.11        1.7330    1   3   4         4
                52.94          2.60        1.7295    0   5   1         2
                55.17          1.92        1.6648    2   4   0         4
                57.94          1.13        1.5917    0   3   5         2
                58.43          1.79        1.5795    0   0   6         1
                58.68          4.42        1.5734    3   1   2         4
                58.79          1.85        1.5707    2   4   2         4
                59.10          1.33        1.5631    3   2   1         4
                60.21         10.98        1.5369    0   5   3         2
                60.22          1.29        1.5367    1   4   4         4
                60.92         10.26        1.5209    2   0   5         2
                60.98         27.95        1.5194    1   3   5         4
                61.72          2.39        1.5029    3   2   2         4
                61.92          1.09        1.4986    2   1   5         4
                63.13          1.49        1.4728    2   4   3         4
                63.26         18.68        1.4699    3   3   0         4
                63.46          7.88        1.4659    0   6   0         2
                64.11          1.87        1.4526    3   3   1         4
                65.19          1.50        1.4311    2   5   1         4
                65.40          2.91        1.4271    1   2   6         4
                65.95          8.74        1.4165    3   2   3         4
                66.35          1.69        1.4088    1   6   0         4
                67.67          7.97        1.3845    2   5   2         4
                70.15          1.33        1.3415    1   3   6         4
                70.36          2.08        1.3381    0   1   7         2
                71.72          4.98        1.3161    2   5   3         4
                73.12          2.75        1.2942    1   1   7         4
                74.70          1.49        1.2707    2   6   0         4
                75.25          1.76        1.2628    4   0   1         2
                75.49          1.13        1.2594    2   6   1         4
                76.22          2.00        1.2491    3   3   4         4
                78.49          3.10        1.2186    4   1   2         4
                81.19          1.39        1.1847    2   1   7         4
                87.02          1.94        1.1198    2   6   4         4
                87.38          2.03        1.1161    1   2   8         4
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.