Sanidine
Gering E
Dissertation Kernforshungszentrum Karlsruhe 1 (1985) 1-97
Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen
Note: Sample SVG3, T = 950 C, neutron diffraction
Locality: Madagascar
_database_code_amcsd 0020578
8.546 13.033 7.176 90 115.97 90 C2/m
atom      x      y      z  occ U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3)
K1M   .2854      0  .1379       .0171   .067   .033      0  .0070      0
SiT1 .00948 .18448 .22362 .726  .0096  .0117  .0077 -.0022  .0040 -.0008
AlT1 .00948 .18448 .22362 .274  .0096  .0117  .0077 -.0022  .0040 -.0008
SiT2 .20784 .38217 .34427 .774  .0093  .0087  .0101  .0004  .0035  .0001
AlT2 .20784 .38217 .34427 .226  .0093  .0087  .0101  .0004  .0035  .0001
Oa1       0 .14630      0       .0260  .0203  .0146      0  .0105      0
Oa2  .63354      0 .28499       .0184  .0128  .0243      0  .0037      0
Ob   .82849 .14543 .22644       .0185  .0319  .0244 -.0046  .0129   .003
Oc   .03317 .30945 .25685       .0167  .0156  .0214 -.0020  .0066 -.0021
Od   .18076 .12654 .40339       .0187  .0206  .0135  .0022  .0026  .0018