Sanidine
Gering E
Dissertation Kernforshungszentrum Karlsruhe 1 (1985) 1-97
Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen
Note: Sample SAGT, T = 1050 C, neutron diffraction
Locality: Madagascar
_database_code_amcsd 0020580
8.546 13.033 7.176 90 115.97 90 C2/m
atom      x      y      z  occ U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3)
K1M   .2851      0  .1381       .0170   .077   .034      0  .0073      0
SiT1 .00946 .18453 .22357 .726  .0100  .0111  .0081 -.0024  .0044 -.0011
AlT1 .00946 .18453 .22357 .274  .0100  .0111  .0081 -.0024  .0044 -.0011
SiT2 .20797 .38216 .34427 .774  .0097  .0082  .0106  .0006  .0037  .0000
AlT2 .20797 .38216 .34427 .226  .0097  .0082  .0106  .0006  .0037  .0000
Oa1       0 .14632      0       .0268  .0199  .0147      0  .0106      0
Oa2  .63384      0 .28483       .0186  .0122  .0244      0  .0040      0
Ob   .82854 .14548 .22655       .0193  .0314  .0246 -.0049  .0132  .0002
Oc   .03327 .30954 .25693       .0171  .0152  .0216 -.0021  .0066 -.0020
Od   .18073 .12654 .40350       .0193  .0204  .0136  .0021  .0033  .0017