Lithiophosphate
Bondareva O S, Simonov M A, Belov N V
Doklady Akademii Nauk SSSR 240 (1978) 75-77
The crystal structure of the synthetic analogue of the lithiophospate
gamma-Li3PO4
Note: this is the quenchable high-temperature form
_database_code_amcsd 0012460
CELL PARAMETERS: 4.9260 6.1290 10.4830 90.000 90.000 90.000
SPACE GROUP: Pcmn
X-RAY WAVELENGTH: 1.541838
Cell Volume: 316.497
Density (g/cm3): 2.430
MAX. ABS. INTENSITY / VOLUME**2: 7.257279762
RIR: 0.973
RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
2-THETA INTENSITY D-SPACING H K L Multiplicity
16.92 25.90 5.2415 0 0 2 2
19.91 5.10 4.4583 1 0 1 4
22.32 100.00 3.9835 0 1 2 4
23.17 90.51 3.8396 1 1 0 4
24.69 16.34 3.6054 1 1 1 8
24.80 50.90 3.5896 1 0 2 4
28.82 14.68 3.0974 1 1 2 8
29.14 15.97 3.0645 0 2 0 2
31.39 1.40 2.8501 1 0 3 4
33.88 59.90 2.6455 0 2 2 4
34.21 29.92 2.6207 0 0 4 2
34.71 30.28 2.5843 1 1 3 8
35.55 14.93 2.5254 1 2 1 8
36.48 47.80 2.4630 2 0 0 2
37.32 1.53 2.4097 0 1 4 4
38.93 1.77 2.3137 1 0 4 4
41.73 2.06 2.1646 1 1 4 8
43.18 4.21 2.0949 2 1 2 8
43.36 5.10 2.0870 1 2 3 8
47.11 4.19 1.9291 1 0 5 4
48.19 1.50 1.8884 2 2 1 8
49.05 4.81 1.8573 1 3 1 8
49.35 3.18 1.8465 1 2 4 8
49.54 2.72 1.8401 1 1 5 8
50.64 14.16 1.8027 2 2 2 8
50.88 5.95 1.7948 2 0 4 4
51.47 7.28 1.7756 1 3 2 8
54.54 1.25 1.6826 2 2 3 8
54.62 3.37 1.6802 0 1 6 4
55.33 6.42 1.6605 1 3 3 8
55.83 2.14 1.6467 1 0 6 4
56.36 2.17 1.6326 1 2 5 8
57.17 4.29 1.6113 0 3 4 4
57.75 1.18 1.5965 2 0 5 4
58.00 1.02 1.5903 1 1 6 8
58.16 4.73 1.5861 3 1 0 4
58.89 2.66 1.5682 3 1 1 8
58.94 3.40 1.5669 3 0 2 4
60.41 12.03 1.5323 0 4 0 2
61.04 1.28 1.5181 3 1 2 8
61.05 22.76 1.5178 0 2 6 4
62.50 1.01 1.4861 3 0 3 4
63.23 1.59 1.4707 0 4 2 4
64.52 11.54 1.4443 3 1 3 8
65.04 1.09 1.4340 2 3 3 8
65.05 5.22 1.4337 3 2 1 8
66.33 1.27 1.4092 1 4 2 8
67.48 1.42 1.3880 2 1 6 8
70.41 4.61 1.3372 3 2 3 8
71.30 2.75 1.3228 0 4 4 4
72.68 5.22 1.3010 2 4 0 4
73.22 2.74 1.2927 3 0 5 4
73.26 10.03 1.2922 2 2 6 8
73.93 4.49 1.2821 1 3 6 8
73.97 2.73 1.2814 0 1 8 4
74.72 4.11 1.2704 3 3 1 8
74.96 1.21 1.2670 3 2 4 8
75.10 2.67 1.2649 3 1 5 8
76.64 1.18 1.2433 3 3 2 8
79.80 6.37 1.2018 3 3 3 8
79.96 1.10 1.1998 1 4 5 8
80.46 3.31 1.1936 0 5 2 4
80.67 1.53 1.1911 3 2 5 8
80.80 3.31 1.1895 1 5 0 4
82.40 4.16 1.1703 1 2 8 8
82.84 1.20 1.1653 2 4 4 8
83.17 1.49 1.1615 4 0 3 4
84.01 1.21 1.1520 0 4 6 4
85.48 1.54 1.1360 4 2 1 8
86.41 1.13 1.1261 1 5 3 8
88.33 1.34 1.1065 3 0 7 4
88.68 4.08 1.1030 0 3 8 4
================================================================================
XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.