Kalgoorlieite
      Kanischeva A S, Mikhailov Y N, Chernov A P
      Izvestiya Akademii Nauk SSSR Neorganicheskie Materialy 18 (1982) 949-952
      Crystal structure of arsenic telluride As2Te3
      Locality: Synthetic
      _database_code_amcsd 0020522

      CELL PARAMETERS:   14.3640   4.0250   9.8890   90.000   95.140   90.000
      SPACE GROUP: C2/m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    569.434
      Density (g/cm3):      6.212
      MAX. ABS. INTENSITY / VOLUME**2:      152.4307225    
      RIR:      7.990
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                12.37          5.30        7.1531    2   0   0         2
                15.95          3.54        5.5559    2   0   1         2
                20.96          2.94        4.2375   -2   0   2         2
                24.48          4.21        3.6358   -1   1   1         4
                27.16         10.26        3.2831    0   0   3         2
                27.28         11.43        3.2691    4   0   1         2
                29.03          5.51        3.0758    3   1   0         4
                29.52         50.99        3.0256   -4   0   2         2
                29.68        100.00        3.0098    1   1   2         4
                29.93          7.16        2.9855   -3   1   1         4
                30.95          2.86        2.8889    3   1   1         4
                32.22          1.62        2.7780    4   0   2         2
                35.29          5.66        2.5436    3   1   2         4
                38.02          2.08        2.3664   -6   0   1         2
                38.61         31.90        2.3321    5   1   0         4
                38.86          1.43        2.3174    4   0   3         2
                39.77         13.40        2.2666    2   0   4         2
                40.53          2.51        2.2257   -6   0   2         2
                41.37          4.76        2.1826    3   1   3         4
                43.63          4.88        2.0744    6   0   2         2
                45.05         16.59        2.0125    0   2   0         2
                45.86         28.83        1.9788   -3   1   4         4
                46.62          3.52        1.9483    4   0   4         2
                49.57          4.43        1.8389    5   1   3         4
                50.05          5.80        1.8223    7   1   0         4
                50.18          1.22        1.8180   -7   1   1         4
                50.86          1.51        1.7952   -6   0   4         2
                51.07          1.03        1.7883    8   0   0         2
                51.09          1.34        1.7879   -8   0   1         2
                51.74          4.58        1.7668    7   1   1         4
                52.11          3.00        1.7553   -7   1   2         4
                52.63          5.07        1.7390    1   1   5         4
                53.40          2.73        1.7158    0   2   3         4
                53.47          3.08        1.7138    4   2   1         4
                54.78         14.90        1.6757   -4   2   2         4
                55.21          1.81        1.6636    4   0   5         2
                55.70          1.47        1.6502   -7   1   3         4
                56.28          3.35        1.6346    8   0   2         2
                56.37          5.66        1.6321   -2   0   6         2
                61.20          1.80        1.5145    8   0   3         2
                61.27          3.13        1.5128   -8   0   4         2
                61.63          6.16        1.5049    2   2   4         4
                62.19          1.20        1.4927   -6   2   2         4
                64.25          2.47        1.4497   -9   1   2         4
                64.51          2.53        1.4444    6   2   2         4
                66.04          2.06        1.4146    3   1   6         4
                66.84          2.04        1.3998    4   2   4         4
                72.20          1.61        1.3084   -3   1   7         4
                72.84          2.64        1.2985    5   1   6         4
                73.63          5.18        1.2865    1   3   2         4
                73.92          1.26        1.2822    4   2   5         4
                74.67          4.21        1.2712   -7   1   6         4
                74.83          2.46        1.2688    8   2   2         4
                74.91          4.12        1.2677   -2   2   6         4
                76.80          1.66        1.2411  -11   1   1         4
                77.99          1.96        1.2252  -11   1   2         4
                78.13          2.67        1.2233    9   1   4         4
                78.79          2.80        1.2147    5   3   0         4
                79.15          1.46        1.2101    8   2   3         4
                79.21          2.53        1.2093   -8   2   4         4
                80.58          1.16        1.1922   12   0   0         2
                81.45          1.82        1.1816   -1   1   8         4
                82.64          1.02        1.1676    5   1   7         4
                83.71          3.61        1.1553   -3   3   4         4
                85.30          1.09        1.1378    9   1   5         4
                85.45          1.32        1.1362   -6   0   8         2
================================================================================