F3.2 Fe0.8 Zr0.2
      Ruchaud N, Grannec J, Hagenmuller P, Soubeyroux J
      Journal of Alloys and Compounds 183 (1992) 263-270
      A neutron diffraction study of the anion-excess cubic ReO3-type
      derived phase Fe.8Zr.2F3.2
      _cod_database_code 1008534
      _database_code_amcsd 0016427

      CELL PARAMETERS:    7.6827   7.6827   7.6827   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    453.463
      Density (g/cm3):     10.872
      MAX. ABS. INTENSITY / VOLUME**2:      742.0765896    
      RIR:     22.225
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                23.15        100.00        3.8414    2   0   0         6
                32.98         23.45        2.7162    2   2   0        12
                40.68          1.06        2.2178    2   2   2         8
                47.33         23.18        1.9207    4   0   0         6
                53.33         33.14        1.7179    4   2   0        24
                58.89         10.35        1.5682    4   2   2        24
                69.17          9.54        1.3581    4   4   0        12
                74.04          8.92        1.2804    4   4   2        24
                74.04          1.70        1.2804    6   0   0         6
                78.79          3.17        1.2147    6   2   0        24
                83.46          1.11        1.1582    6   2   2        24
                88.09          2.62        1.1089    4   4   4         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.