Marokite
      Zouari S, Ranno L, Cheikh-Rouhou A, Isnard O, Pernet M, Wolfers P, Strobel P
      Journal of Alloys and Compounds 353 (2003) 5-11
      New model for the magnetic structure of the marokite-type oxide CaMn2O4
      Locality: synthetic
      Sample: T = 280 K
      _database_code_amcsd 0012829

      CELL PARAMETERS:    3.1492   9.9800   9.6600   90.000   90.000   90.000
      SPACE GROUP: Pbcm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    303.604
      Density (g/cm3):      4.680
      MAX. ABS. INTENSITY / VOLUME**2:      26.46625675    
      RIR:      1.841
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.37         24.15        4.8300    0   0   2         2
                20.03          2.63        4.4334    0   2   1         4
                25.67          8.79        3.4705    0   2   2         4
                28.34          1.06        3.1492    1   0   0         2
                29.75         21.58        3.0032    1   1   0         4
                31.19         27.28        2.8678    1   1   1         8
                33.11        100.00        2.7056    0   2   3         4
                33.65          4.87        2.6632    1   2   0         4
                33.98          2.02        2.6380    1   0   2         4
                34.95         10.11        2.5674    1   2   1         8
                35.19         33.42        2.5504    1   1   2         8
                36.00         24.74        2.4950    0   4   0         2
                37.23          2.29        2.4150    0   0   4         2
                38.61          2.37        2.3322    1   2   2         8
                39.40         37.84        2.2870    1   3   0         4
                40.54         58.25        2.2255    1   3   1         8
                41.10          3.50        2.1962    1   1   3         8
                41.54         15.80        2.1738    0   2   4         4
                43.80         44.62        2.0670    1   3   2         8
                47.44          2.51        1.9164    1   0   4         4
                48.36          6.02        1.8820    1   1   4         8
                48.84          3.17        1.8646    1   3   3         8
                50.34          6.16        1.8127    1   4   2         8
                50.67          8.05        1.8017    0   2   5         4
                52.75          1.17        1.7353    0   4   4         4
                55.32          4.05        1.6608    1   5   1         8
                55.32          2.26        1.6606    1   3   4         8
                56.65         24.65        1.6248    1   1   5         8
                57.22         11.92        1.6100    0   0   6         2
                57.94          8.59        1.5917    1   5   2         8
                58.63         11.76        1.5746    2   0   0         2
                58.71          7.40        1.5727    0   6   2         4
                59.07          3.80        1.5638    1   2   5         8
                59.43          6.84        1.5554    2   1   0         4
                60.62          1.65        1.5276    0   4   5         4
                62.15         23.72        1.4936    1   5   3         8
                62.89         17.01        1.4778    0   6   3         4
                62.98         12.24        1.4759    1   3   5         8
                65.05          1.54        1.4339    2   2   2         8
                65.59          1.48        1.4232    2   3   0         4
                65.82          3.11        1.4190    1   1   6         8
                66.80          2.08        1.4005    2   1   3         8
                69.01         11.55        1.3609    2   2   3         8
                69.48          7.67        1.3528    0   4   6         4
                70.75          4.99        1.3316    2   4   0         4
                70.85          1.71        1.3301    0   2   7         4
                71.69          3.18        1.3165    1   3   6         8
                72.25          1.31        1.3076    2   1   4         8
                72.63          3.16        1.3017    2   3   3         8
                72.82          2.35        1.2988    1   7   0         4
                73.58          1.10        1.2872    1   7   1         8
                73.82          1.29        1.2837    2   4   2         8
                74.73          3.93        1.2703    1   5   5         8
                75.85          2.43        1.2543    1   7   2         8
                76.34          2.32        1.2475    0   8   0         2
                77.09          2.27        1.2372    0   8   1         4
                79.32          1.84        1.2079    0   8   2         4
                81.12          2.48        1.1856    2   2   5         8
                81.45          1.91        1.1816    1   3   7         8
                83.82          2.29        1.1541    2   5   3         8
                86.44          4.28        1.1257    2   0   6         4
                86.96          4.18        1.1203    1   1   8         8
                87.13          1.23        1.1186    2   1   6         8
                87.71          1.20        1.1127    2   6   2         8
================================================================================