Cadmium
      Jette E R, Foote F
      Journal of Chemical Physics 3 (1935) 605-616
      Precision determination of lattice constants
      Locality: synthetic
      Sample: at T = 25 C
      Note: lattice parameter is average of two samples
      _database_code_amcsd 0012941

      CELL PARAMETERS:    2.9731   2.9731   5.6069   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     42.921
      Density (g/cm3):      8.697
      MAX. ABS. INTENSITY / VOLUME**2:      407.8785086    
      RIR:     15.271
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                31.92         38.25        2.8035    0   0   2         2
                34.84         22.35        2.5748    1   0   0         6
                38.47        100.00        2.3399    1   0   1        12
                47.97         16.54        1.8963    1   0   2        12
                61.29         21.27        1.5125    1   0   3        12
                62.48         13.24        1.4865    1   1   0         6
                66.73          3.49        1.4017    0   0   4         2
                71.89         16.15        1.3133    1   1   2        12
                73.57          1.86        1.2874    2   0   0         6
                75.82         10.11        1.2547    2   0   1        12
                77.54          3.13        1.2311    1   0   4        12
                82.44          2.58        1.1699    2   0   2        12
================================================================================