Gallium
      Bosio L
      Journal of Chemical Physics 68 (1978) 1221-1223
      Crystal structures of Ga(II) and Ga(III)
      Locality: synthetic
      Sample: at P = 2.8 GPa, T = 298 K
      Note: structure known as Ga(III) phase
      _database_code_amcsd 0013006

      CELL PARAMETERS:    2.8130   2.8130   4.4520   90.000   90.000   90.000
      SPACE GROUP: I4/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     35.229
      Density (g/cm3):      6.572
      MAX. ABS. INTENSITY / VOLUME**2:      240.8101115    
      RIR:     11.931
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                37.83        100.00        2.3781    1   0   1         8
                40.53         20.44        2.2260    0   0   2         2
                45.61         28.57        1.9891    1   1   0         4
                62.63         20.15        1.4832    1   1   2         8
                66.48          8.22        1.4065    2   0   0         4
                71.94         12.57        1.3126    1   0   3         8
                79.11         18.46        1.2106    2   1   1        16
                80.84          8.64        1.1890    2   0   2         8
                87.68          1.72        1.1130    0   0   4         2
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.