Gallium
      Bosio L
      Journal of Chemical Physics 68 (1978) 1221-1223
      Crystal structures of Ga(II) and Ga(III)
      Loclailty: synthetic
      Sample: at P = 2.6 GPa, T = 313 K
      Note: structure known as Ga(II) phase
      _database_code_amcsd 0013007

      CELL PARAMETERS:    5.9510   5.9510   5.9510   90.000   90.000   90.000
      SPACE GROUP: I-43d     
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    210.751
      Density (g/cm3):      6.591
      MAX. ABS. INTENSITY / VOLUME**2:      258.2034724    
      RIR:     12.755
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                37.00        100.00        2.4295    2   1   1        12
                42.99         10.71        2.1040    2   2   0        12
                48.37         29.72        1.8819    3   1   0        24
                57.99         16.39        1.5905    3   2   1        24
                62.42          1.59        1.4878    4   0   0         6
                70.81         16.58        1.3307    4   2   0        24
                74.83         10.34        1.2688    3   3   2        12
                78.79          2.92        1.2147    4   2   2        12
                82.68         10.10        1.1671    4   3   1        24
                82.68          5.05        1.1671    5   1   0        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.