Nickel
      Suh I-K, Ohta H, Waseda Y
      Journal of Materials Science 23 (1988) 757-760
      High-temperature thermal expansion of six metallic elements measured
      by dilatation method and X-ray diffraction
      Locality: synthetic
      Sample: at T = 1007 K
      _database_code_amcsd 0013101

      CELL PARAMETERS:    3.5630   3.5630   3.5630   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     45.232
      Density (g/cm3):      8.618
      MAX. ABS. INTENSITY / VOLUME**2:      285.7957841    
      RIR:     10.799
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                44.02        100.00        2.0571    1   1   1         8
                51.28         45.39        1.7815    2   0   0         6
                75.47         23.17        1.2597    2   2   0        12
================================================================================