Nickel
      Suh I-K, Ohta H, Waseda Y
      Journal of Materials Science 23 (1988) 757-760
      High-temperature thermal expansion of six metallic elements measured
      by dilatation method and X-ray diffraction
      Locality: synthetic
      Sample: at T = 1433 K
      _database_code_amcsd 0013105

      CELL PARAMETERS:    3.5950   3.5950   3.5950   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     46.462
      Density (g/cm3):      8.390
      MAX. ABS. INTENSITY / VOLUME**2:      279.0744192    
      RIR:     10.831
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                43.61        100.00        2.0756    1   1   1         8
                50.79         45.51        1.7975    2   0   0         6
                74.68         23.32        1.2710    2   2   0        12
================================================================================