F5 Fe H4 Mn O2
Laligant Y, Pannetier J, Ferey G
Journal of Solid State Chemistry 66 (1987) 242-250
Ordered magnetic frustration. VI. Crystal and magnetic structures of
the inverse Weberites Zn Fe F5 (H2 O)2 and Mn Fe F5 (H2 O)2
at 1.5K from powder neutron diffraction
_cod_database_code 1000230
_database_code_amcsd 0013592
7.475 10.766 6.594 90 90 90 Imm2
atom    x    y    z
Mn1     0  .75  .75
Fe1   .25    0    0
F1   .291 .873 .198
F2   .709 .626 .302
F3      0    0 .073
F4      0   .5 .427
O1     .5 .321 .945
O2     .5 .179 .554
H1   .101 .840 .363
H2   .897 .660 .138