Marokite
      Ling C D, Neumeier J J, Argyriou D N
      Journal of Solid State Chemistry 160 (2001) 167-173
      Observation of antiferromagnetism in marokite CaMn2O4
      Locality: synthetic
      Sample: T = 300 K
      _database_code_amcsd 0014005

      CELL PARAMETERS:    3.1589   9.9958   9.6776   90.000   90.000   90.000
      SPACE GROUP: Pbcm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    305.573
      Density (g/cm3):      4.650
      MAX. ABS. INTENSITY / VOLUME**2:      27.48988540    
      RIR:      1.925
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                17.75          1.74        4.9979    0   2   0         2
                18.33         22.00        4.8388    0   0   2         2
                19.99          2.96        4.4407    0   2   1         4
                25.62          8.37        3.4764    0   2   2         4
                28.25          1.04        3.1589    1   0   0         2
                29.66         22.52        3.0120    1   1   0         4
                31.10         29.32        2.8760    1   1   1         8
                33.05        100.00        2.7103    0   2   3         4
                33.56          5.55        2.6702    1   2   0         4
                33.89          2.14        2.6451    1   0   2         4
                34.85         10.75        2.5740    1   2   1         8
                35.09         32.00        2.5571    1   1   2         8
                35.94         25.69        2.4990    0   4   0         2
                37.16          1.77        2.4194    0   0   4         2
                38.51          2.70        2.3379    1   2   2         8
                39.30         38.17        2.2924    1   3   0         4
                40.44         56.79        2.2307    1   3   1         8
                41.00          4.10        2.2015    1   1   3         8
                41.47         15.43        2.1777    0   2   4         4
                43.69         45.59        2.0717    1   3   2         8
                47.33          3.06        1.9208    1   0   4         4
                48.25          6.34        1.8862    1   1   4         8
                48.73          3.12        1.8686    1   3   3         8
                50.23          6.62        1.8165    1   4   2         8
                50.57          8.01        1.8049    0   2   5         4
                52.66          1.01        1.7382    0   4   4         4
                55.20          5.16        1.6641    1   5   1         8
                55.20          3.25        1.6641    1   3   4         8
                56.52         25.52        1.6283    1   1   5         8
                57.10         13.43        1.6129    0   0   6         2
                57.81          7.61        1.5949    1   5   2         8
                58.43         12.03        1.5794    2   0   0         2
                58.60          8.01        1.5752    0   6   2         4
                58.94          4.17        1.5671    1   2   5         8
                59.23          7.36        1.5601    2   1   0         4
                60.50          1.72        1.5302    0   4   5         4
                62.01         25.68        1.4965    1   5   3         8
                62.77         18.78        1.4802    0   6   3         4
                62.84         12.42        1.4789    1   3   5         8
                64.84          1.78        1.4380    2   2   2         8
                65.39          1.99        1.4272    2   3   0         4
                65.66          3.85        1.4219    1   1   6         8
                66.58          2.38        1.4045    2   1   3         8
                68.79         12.81        1.3646    2   2   3         8
                69.34          9.16        1.3552    0   4   6         4
                70.54          5.91        1.3351    2   4   0         4
                70.70          1.45        1.3325    0   2   7         4
                71.52          4.24        1.3191    1   3   6         8
                72.03          1.29        1.3111    2   1   4         8
                72.41          3.63        1.3052    2   3   3         8
                72.66          2.64        1.3012    1   7   0         4
                73.43          1.19        1.2896    1   7   1         8
                73.60          1.54        1.2870    2   4   2         8
                74.56          4.92        1.2727    1   5   5         8
                75.69          3.39        1.2566    1   7   2         8
                76.19          2.63        1.2495    0   8   0         2
                76.94          2.51        1.2392    0   8   1         4
                79.17          1.75        1.2098    0   8   2         4
                80.87          3.00        1.1886    2   2   5         8
                81.26          2.31        1.1839    1   3   7         8
                82.85          1.04        1.1651    0   8   3         4
                83.58          3.13        1.1569    2   5   3         8
                86.18          5.33        1.1285    2   0   6         4
                86.75          4.63        1.1225    1   1   8         8
                86.86          1.63        1.1214    2   1   6         8
                87.45          1.38        1.1153    2   6   2         8
================================================================================