Magnesium
      Raynor G V, Hume-Rothery W
      Journal of the Institute of Metals 65 (1939) 477-485
      A technique for the X-ray powder photography of reactive metals and alloys
      with special reference to the lattice spacing of magnesium at high temperatures
      Locality: synthetic
      Sample: at T = 31.4 C
      Note: experiment #7
      _database_code_amcsd 0014117

      CELL PARAMETERS:    3.2036   3.2036   5.2017   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     46.233
      Density (g/cm3):      1.746
      MAX. ABS. INTENSITY / VOLUME**2:      20.67577284    
      RIR:      3.857
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                32.27         24.18        2.7744    1   0   0         6
                34.48         26.66        2.6009    0   0   2         2
                36.71        100.00        2.4480    1   0   1        12
                47.94         14.63        1.8975    1   0   2        12
                57.54         15.71        1.6018    1   1   0         6
                63.24         16.78        1.4704    1   0   3        12
                67.52          2.20        1.3872    2   0   0         6
                68.84         16.41        1.3639    1   1   2        12
                70.22         11.44        1.3404    2   0   1        12
                72.71          2.24        1.3004    0   0   4         2
                78.08          2.61        1.2240    2   0   2        12
                81.80          2.22        1.1775    1   0   4        12
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.