Magnesium
      Raynor G V, Hume-Rothery W
      Journal of the Institute of Metals 65 (1939) 477-485
      A technique for the X-ray powder photography of reactive metals and alloys
      with special reference to the lattice spacing of magnesium at high temperatures
      Locality: synthetic
      Sample: at T = 160 C
      Note: experiment #2
      _database_code_amcsd 0014118

      CELL PARAMETERS:    3.2147   3.2147   5.2203   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     46.720
      Density (g/cm3):      1.727
      MAX. ABS. INTENSITY / VOLUME**2:      20.46199128    
      RIR:      3.857
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                32.15         24.17        2.7840    1   0   0         6
                34.36         26.66        2.6102    0   0   2         2
                36.58        100.00        2.4565    1   0   1        12
                47.76         14.65        1.9042    1   0   2        12
                57.32         15.76        1.6073    1   1   0         6
                62.99         16.84        1.4756    1   0   3        12
                67.26          2.21        1.3920    2   0   0         6
                68.56         16.47        1.3687    1   1   2        12
                69.94         11.49        1.3450    2   0   1        12
                72.41          2.25        1.3051    0   0   4         2
                77.75          2.62        1.2283    2   0   2        12
                81.44          2.23        1.1817    1   0   4        12
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs