Magnesium
      Raynor G V, Hume-Rothery W
      Journal of the Institute of Metals 65 (1939) 477-485
      A technique for the X-ray powder photography of reactive metals and alloys
      with special reference to the lattice spacing of magnesium at high temperatures
      Locality: synthetic
      Sample: at T = 597 C
      Note: experiment #9
      _database_code_amcsd 0014122

      CELL PARAMETERS:    3.2599   3.2599   5.2960   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     48.740
      Density (g/cm3):      1.656
      MAX. ABS. INTENSITY / VOLUME**2:      19.61869797    
      RIR:      3.858
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                31.69         24.12        2.8232    1   0   0         6
                33.85         26.66        2.6480    0   0   2         2
                36.05        100.00        2.4913    1   0   1        12
                47.05         14.74        1.9314    1   0   2        12
                56.45         15.94        1.6300    1   1   0         6
                62.00         17.10        1.4968    1   0   3        12
                66.21          2.24        1.4116    2   0   0         6
                67.48         16.74        1.3881    1   1   2        12
                68.83         11.67        1.3640    2   0   1        12
                71.22          2.29        1.3240    0   0   4         2
                76.47          2.66        1.2456    2   0   2        12
                80.05          2.27        1.1987    1   0   4        12
                88.74          4.90        1.1025    2   0   3        12
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.