Indium
      Smith J F, Schneider V L
      Journal of the Less-Common Metals 7 (1964) 17-22
      Anisotropic thermal expansion of indium
      Sample: .2 atomic % lead
      Note: converted from kx units
      Locality: synthetic
      _database_code_amcsd 0014131

      CELL PARAMETERS:    3.2523   3.2523   4.9490   90.000   90.000   90.000
      SPACE GROUP: I4/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     52.348
      Density (g/cm3):      7.283
      MAX. ABS. INTENSITY / VOLUME**2:      397.0610879    
      RIR:     17.751
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                32.96        100.00        2.7179    1   0   1         8
                36.30         18.93        2.4745    0   0   2         2
                39.17         30.19        2.2997    1   1   0         4
                54.47         20.75        1.6846    1   1   2         8
                56.60          9.08        1.6262    2   0   0         4
                63.20         12.32        1.4712    1   0   3         8
                67.07         19.98        1.3955    2   1   1        16
                69.12          8.99        1.3590    2   0   2         8
                77.08          1.55        1.2372    0   0   4         2
                84.20          2.36        1.1499    2   2   0         4
                89.92          7.91        1.0910    2   1   3        16
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.