Okamura K
Journal of the Physical Society of Japan 28 (1970) 1005-1014
Lattice modulation in the long period ordered alloys studied by X-ray diffraction. III. Cu3Pd
Locality: synthetic
Note: Coordinates of Cu6 altered to reproduce reported bond lengths
_database_code_amcsd 0014169
3.710 3.710 25.655 90 90 90 P4mm
atom  x  y      z Biso
Cu1  .5  0  .0714  .92
Cu2  .5  0  .2143  .91
Cu3  .5  0  .3571  .92
Cu4  .5  0  .5000  .67
Cu5  .5  0  .6428  .92
Cu6  .5  0  .7857  .92
Cu7  .5  0  .9286  .92
Cu8  .5 .5  .0003  .92
Cu9  .5 .5  .1433 1.33
Cu10 .5 .5  .2854 1.27
Cu11 .5 .5  .4280  .88
Cu12  0  0  .5717 1.16
Cu13  0  0  .7143 1.27
Cu14  0  0  .8586 1.15
Pd15  0  0 -.0004  .73
Pd16  0  0  .1427  .68
Pd17  0  0  .2859  .69
Pd18  0  0  .4290  .84
Pd19 .5 .5  .5714  .78
Pd20 .5 .5  .7144  .73
Pd21 .5 .5  .8573  .79