Nielsenite
      Okamura K
      Journal of the Physical Society of Japan 28 (1970) 1005-1014
      Lattice modulation in the long period ordered alloys studied by X-ray diffraction. III. Cu3Pd
      Locality: synthetic
      Note: Coordinates of Cu6 altered to reproduce reported bond lengths
      _database_code_amcsd 0014169

      CELL PARAMETERS:    3.7100   3.7100  25.6550   90.000   90.000   90.000
      SPACE GROUP: P4mm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    353.118
      Density (g/cm3):      9.777
      MAX. ABS. INTENSITY / VOLUME**2:      376.3537849    
      RIR:     12.534
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                24.24          3.41        3.6718    1   0   1         4
                24.29          2.00        3.6650    0   0   7         1
                31.94          1.77        2.8022    1   0   6         4
                34.18          1.56        2.6234    1   1   0         4
                37.05          1.02        2.4261    1   0   8         4
                42.37        100.00        2.1332    1   1   7         4
                49.11         30.82        1.8550    2   0   0         4
                49.76         14.73        1.8325    0   0  14         1
                71.99          7.90        1.3117    2   2   0         4
                72.51         15.39        1.3037    2   0  14         4
                87.25         16.94        1.1174    3   1   7         8
                88.23          8.20        1.1075    1   1  21         4
================================================================================