Li1.2 O4 Ti1.8
      Deschanvres A, Raveau B, Sekkal Z
      Materials Research Bulletin 6 (1971) 699-704
      Mise en evidence et etude cristallographique d'une nouvelle solution
      solide de type spinelle Li1+x Ti2-x O4  0<X<0,333
      _cod_database_code 1001099
      _database_code_amcsd 0014219

      CELL PARAMETERS:    8.3590   8.3590   8.3590   90.000   90.000   90.000
      SPACE GROUP: Fd3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    584.067
      Density (g/cm3):      3.604
      MAX. ABS. INTENSITY / VOLUME**2:      42.42366364    
      RIR:      3.833
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.38        100.00        4.8261    1   1   1         8
                35.62         41.44        2.5203    3   1   1        24
                37.26          3.46        2.4130    2   2   2         8
                43.30         56.98        2.0898    4   0   0         6
                47.41          6.51        1.9177    3   3   1        24
                57.27         16.92        1.6087    5   1   1        24
                57.27          1.06        1.6087    3   3   3         8
                62.89         30.39        1.4777    4   4   0        12
                66.13         10.50        1.4129    5   3   1        48
                74.42          3.51        1.2747    5   3   3        24
                75.43          2.85        1.2602    6   2   2        24
                79.43          6.71        1.2065    4   4   4         8
                82.39          4.13        1.1705    5   5   1        24
                82.39          1.02        1.1705    7   1   1        24
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs