Fayalite
      Kudoh Y, Takeda H
      Physica B 140 (1986) 333-336
      Single crystal X-ray diffraction study on the bond compressibility
      of fayalite, Fe2SiO4 and rutile, TiO2 under high pressure
      Sample: P = 117 kbar
      _database_code_amcsd 0015003

      CELL PARAMETERS:    4.7560  10.0890   5.9760   90.000   90.000   90.000
      SPACE GROUP: Pbnm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    286.748
      Density (g/cm3):      4.719
      MAX. ABS. INTENSITY / VOLUME**2:      22.85451094    
      RIR:      1.577
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                17.58          2.25        5.0445    0   2   0         2
                20.65         15.40        4.3020    1   1   0         4
                23.07         15.74        3.8548    0   2   1         4
                23.91          5.63        3.7213    1   0   1         4
                25.51         68.02        3.4914    1   1   1         8
                25.74          2.57        3.4605    1   2   0         4
                29.84          5.27        2.9947    1   2   1         8
                29.90          5.69        2.9880    0   0   2         2
                32.61         75.67        2.7459    1   3   0         4
                34.90         30.51        2.5708    0   2   2         4
                35.59         31.41        2.5222    0   4   0         2
                35.99         68.38        2.4951    1   3   1         8
                36.62        100.00        2.4541    1   1   2         8
                37.83         19.92        2.3780    2   0   0         2
                38.75          7.65        2.3238    0   4   1         4
                38.91         11.24        2.3146    2   1   0         4
                39.86          5.92        2.2616    1   2   2         8
                40.48          8.99        2.2283    1   4   0         4
                41.85          8.69        2.1583    2   1   1         8
                42.00          1.07        2.1510    2   2   0         4
                44.83         15.98        2.0218    1   3   2         8
                47.15          3.15        1.9274    0   4   2         4
                49.04          3.01        1.8575    1   5   0         4
                50.49         13.36        1.8076    1   1   3         8
                51.52          7.26        1.7738    1   5   1         8
                52.41         76.40        1.7457    2   2   2         8
                52.92         19.06        1.7302    2   4   0         4
                53.04          5.24        1.7264    1   2   3         8
                55.27          9.23        1.6620    2   4   1         8
                56.88          5.87        1.6186    0   6   1         4
                57.13         17.52        1.6124    1   3   3         8
                58.51         13.58        1.5775    1   5   2         8
                58.98          5.59        1.5661    3   1   0         4
                59.10          6.15        1.5633    0   4   3         4
                61.18          6.18        1.5150    3   1   1         8
                61.29          1.25        1.5124    3   2   0         4
                61.41          1.20        1.5098    2   1   3         8
                61.98          1.17        1.4973    2   4   2         8
                62.13         18.73        1.4940    0   0   4         2
                62.32          1.31        1.4900    2   5   1         8
                63.44          1.48        1.4662    3   2   1         8
                63.48         22.59        1.4654    0   6   2         4
                65.04          5.07        1.4340    3   3   0         4
                66.22          1.67        1.4113    1   1   4         8
                67.13          8.29        1.3944    3   3   1         8
                67.53          9.84        1.3871    3   1   2         8
                67.96         14.03        1.3793    1   7   0         4
                69.15          2.09        1.3585    1   5   3         8
                69.68          3.40        1.3494    3   2   2         8
                70.36          1.48        1.3381    2   6   1         8
                71.95         10.31        1.3123    1   3   4         8
                72.13          2.61        1.3096    3   4   1         8
                72.34          1.22        1.3063    2   4   3         8
                73.70          5.67        1.2854    0   4   4         4
                73.74          4.06        1.2849    0   6   3         4
                75.09          6.86        1.2651    2   0   4         4
                75.78          1.06        1.2552    2   1   4         8
                76.33         12.11        1.2475    2   6   2         8
                76.40          2.50        1.2466    3   5   0         4
                78.56          1.71        1.2176    2   5   3         8
                80.84          3.36        1.1890    4   0   0         2
                82.94          1.90        1.1642    1   5   4         8
                82.97          2.65        1.1638    3   3   3         8
                84.15          8.24        1.1505    3   5   2         8
                85.15          1.50        1.1394    2   7   2         8
                85.96          7.35        1.1308    2   4   4         8
                87.57          3.95        1.1141    2   8   0         4
                87.67          1.22        1.1131    3   4   3         8
                89.17          2.17        1.0982    4   1   2         8
                89.41          3.13        1.0959    1   3   5         8
                89.48          1.53        1.0953    2   8   1         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.