Ca Cu2 La2 O6.037
      Fuertes A, Obradors X, Navarro J, Gomez-Romero P, Casan-Pastor N,
      Perez F, Fontcuberta J, Miravitlles C
      Rodriguez-Carvajal J, Martinez B
      Physica C 170 (1990) 153-160
      Oxygen excess and superconductivity at 45 K in La2 Ca Cu2 O6+y
      _cod_database_code 1006108
      _database_code_amcsd 0015021

      CELL PARAMETERS:    3.8335   3.8335  19.5169   90.000   90.000   90.000
      SPACE GROUP: I4/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    286.815
      Density (g/cm3):      6.270
      MAX. ABS. INTENSITY / VOLUME**2:      106.9700936    
      RIR:      5.555
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                18.18         10.58        4.8792    0   0   4         2
                23.65          3.80        3.7616    1   0   1         8
                27.00         32.39        3.3027    1   0   3         8
                27.42          2.86        3.2528    0   0   6         2
                32.74        100.00        2.7351    1   0   5         8
                33.05         75.89        2.7107    1   1   0         4
                34.34          4.71        2.6118    1   1   2         8
                36.84         10.66        2.4396    0   0   8         2
                39.99         27.90        2.2548    1   0   7         8
                43.46         18.11        2.0824    1   1   6         8
                46.53          3.68        1.9517    0   0  10         2
                47.43         42.01        1.9167    2   0   0         4
                48.21          8.89        1.8875    1   0   9         8
                50.32          8.23        1.8134    1   1   8         8
                51.20          2.29        1.7840    2   0   4         8
                55.42          7.67        1.6578    2   1   3        16
                55.66          1.46        1.6514    2   0   6         8
                56.59          6.88        1.6264    0   0  12         2
                57.21          3.32        1.6102    1   0  11         8
                58.25          3.83        1.5839    1   1  10         8
                58.83         31.00        1.5697    2   1   5        16
                61.53          7.20        1.5072    2   0   8         8
                63.72         10.84        1.4604    2   1   7        16
                67.12          8.20        1.3946    1   1  12         8
                68.63          3.40        1.3675    2   0  10         8
                69.33         10.35        1.3553    2   2   0         4
                69.95          4.70        1.3449    2   1   9        16
                75.88          1.31        1.2539    3   0   3         8
                76.87          8.99        1.2401    2   0  12         8
                76.90          1.03        1.2397    1   1  14         8
                77.41          2.22        1.2329    2   1  11        16
                78.81          5.55        1.2144    3   0   5         8
                78.98          8.50        1.2123    3   1   0         8
                81.19          2.62        1.1848    2   2   8         8
                83.16          2.09        1.1616    3   0   7         8
                85.48          2.86        1.1359    3   1   6        16
                87.66          1.44        1.1132    2   2  10         8
                88.89          1.07        1.1009    3   0   9         8
                89.01          7.06        1.0998    1   0  17         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.