Bi0.33 Ca0.89 Cu2 O7 Sr2 Tl0.78
      Ledesert M, Maignan A, Chardon J, Martin C, Labbe P, Hervieu M, Raveau B
      Physica C 232 (1994) 387-395
      (Tl, Bi) Sr2 Ca Cu2 O7 "1212" superconducting single crystal.
      A structural and magnetic study
      _cod_database_code 1001634
      _database_code_amcsd 0015068

      CELL PARAMETERS:    3.7922   3.7922  12.0661   90.000   90.000   90.000
      SPACE GROUP: P4/mmm    
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    173.520
      Density (g/cm3):      6.491
      MAX. ABS. INTENSITY / VOLUME**2:      126.6056441    
      RIR:      6.351
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                 7.33         18.14       12.0661    0   0   1         2
                14.68          5.14        6.0331    0   0   2         2
                22.10         13.57        4.0220    0   0   3         2
                23.46          8.69        3.7922    1   0   0         4
                24.61         18.80        3.6177    1   0   1         8
                27.79         49.50        3.2106    1   0   2         8
                29.61          5.42        3.0165    0   0   4         2
                32.45        100.00        2.7592    1   0   3         8
                33.42         74.69        2.6815    1   1   0         4
                34.26         10.02        2.6176    1   1   1         8
                36.68          1.76        2.4504    1   1   2         8
                37.26         16.53        2.4132    0   0   5         2
                38.12          7.86        2.3607    1   0   4         8
                40.43          1.52        2.2311    1   1   3         8
                44.50          5.89        2.0359    1   0   5         8
                45.08          5.25        2.0110    0   0   6         2
                45.25         17.06        2.0041    1   1   4         8
                47.98         35.74        1.8961    2   0   0         4
                50.91         15.52        1.7938    1   1   5         8
                51.43          9.48        1.7767    1   0   6         8
                53.13          1.06        1.7237    0   0   7         2
                53.42          2.78        1.7151    2   0   3         8
                54.07          1.05        1.6959    2   1   0         8
                54.65          2.71        1.6794    2   1   1        16
                56.35         11.09        1.6326    2   1   2        16
                57.26          6.96        1.6088    1   1   6         8
                57.40          2.40        1.6053    2   0   4         8
                58.85          7.82        1.5692    1   0   7         8
                59.12         29.58        1.5627    2   1   3        16
                61.48          3.19        1.5083    0   0   8         2
                62.27         10.08        1.4909    2   0   5         8
                62.86          3.50        1.4783    2   1   4        16
                66.74          3.44        1.4015    1   0   8         8
                67.50          2.21        1.3876    2   1   5        16
                67.95          3.93        1.3796    2   0   6         8
                70.20          8.48        1.3407    2   2   0         4
                71.81          3.93        1.3146    1   1   8         8
                72.97          4.81        1.2965    2   1   6        16
                74.38          1.77        1.2755    2   0   7         8
                77.09          1.72        1.2372    3   0   2         8
                79.24          5.13        1.2089    2   1   7        16
                79.48          5.12        1.2059    3   0   3         8
                80.01          7.41        1.1992    3   1   0         8
                80.01          2.45        1.1992    1   1   9         8
                81.55          4.06        1.1804    2   0   8         8
                82.26          3.32        1.1720    2   2   5         8
                86.32          2.56        1.1270    2   1   8        16
                87.43          1.36        1.1156    2   2   6         8
                87.55          2.38        1.1144    3   1   4        16
                88.95          1.55        1.1003    1   1  10         8
                89.54          1.18        1.0947    2   0   9         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs