Ca0.03 Cu La1.97 O4
      Rial C, Moran E, Alario-Franco M, Amador U, Martinez J, Rodriguez-Carvajal J, Andersen N
      Physica C 297 (1998) 277-293
      Effects of extra oxygen on the structure and superconductivity of
      La2-xCaxCuO4+y prepared by chemical oxidation
      _cod_database_code 1006178
      _database_code_amcsd 0015087

      CELL PARAMETERS:    5.3336   5.4000  13.1256   90.000   90.000   90.000
      SPACE GROUP: Bmab      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    378.036
      Density (g/cm3):      7.072
      MAX. ABS. INTENSITY / VOLUME**2:      177.7300879    
      RIR:      8.183
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                13.49          4.22        6.5628    0   0   2         2
                24.42         19.77        3.6454    1   1   1         8
                27.18         11.16        3.2814    0   0   4         2
                31.20        100.00        2.8667    1   1   3         8
                33.18         32.42        2.7000    0   2   0         2
                33.61         32.10        2.6668    2   0   0         2
                41.27         10.15        2.1876    0   0   6         2
                41.84         22.05        2.1589    1   1   5         8
                43.40         11.70        2.0849    0   2   4         4
                43.74         11.52        2.0695    2   0   4         4
                47.95         29.23        1.8973    2   2   0         4
                53.94          4.63        1.6997    0   2   6         4
                54.23          4.68        1.6913    2   0   6         4
                54.24          1.88        1.6913    1   3   1         8
                54.59          8.76        1.6811    1   1   7         8
                54.81          1.75        1.6749    3   1   1         8
                55.98          4.97        1.6425    2   2   4         8
                56.05          4.26        1.6407    0   0   8         2
                58.04         14.88        1.5890    1   3   3         8
                58.59         13.97        1.5754    3   1   3         8
                65.07          7.70        1.4333    2   2   6         8
                65.24          4.32        1.4302    1   3   5         8
                65.75          4.44        1.4202    3   1   5         8
                66.71          3.12        1.4021    0   2   8         4
                66.96          3.03        1.3974    2   0   8         4
                69.65          3.54        1.3500    0   4   0         2
                70.64          3.60        1.3334    4   0   0         2
                75.33          2.68        1.2617    1   3   7         8
                75.81          2.69        1.2548    3   1   7         8
                76.81          5.62        1.2410    2   2   8         8
                78.76          5.13        1.2151    3   3   3         8
                79.59          3.30        1.2045    2   4   0         4
                80.30          3.40        1.1956    4   2   0         4
                84.29          1.44        1.1489    0   4   6         4
                85.15          1.71        1.1395    3   3   5         8
                85.23          1.50        1.1386    4   0   6         4
                85.26          6.51        1.1383    1   1  11         8
                85.97          1.97        1.1307    2   4   4         8
                86.67          1.99        1.1233    4   2   4         8
================================================================================