Cobalt
      Marick L
      Physical Review 49 (1936) 831-837
      Variation of resistance and structure of cobalt with temperature
      and a discussion of its photoelectric emission
      Locality: synthetic
      Sample: at room T
      Note: cell edge a is average of photographs 1 & 2
      _database_code_amcsd 0015136

      CELL PARAMETERS:    2.5190   2.5190   4.0910   90.000   90.000  120.000
      SPACE GROUP: P6_3/mmc  
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     22.481
      Density (g/cm3):      8.705
      MAX. ABS. INTENSITY / VOLUME**2:      233.7473509    
      RIR:      8.743
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                41.39         25.45        2.1815    1   0   0         6
                44.28         27.40        2.0455    0   0   2         2
                47.22        100.00        1.9249    1   0   1        12
                62.22         12.74        1.4922    1   0   2        12
                75.48         12.75        1.2595    1   1   0         6
                83.62         13.69        1.1563    1   0   3        12
                89.95          1.86        1.0908    2   0   0         6
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.