Lithium
      Barrett C S
      Physical Review 72 (1947) 245-245
      A low temperature transformation in lithium
      Locality: synthetic
      Sample: at T = -196 C
      Note: transformation induced by metal being plastically deformed
      _database_code_amcsd 0015148

      CELL PARAMETERS:    4.4100   4.4100   4.4100   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:     85.766
      Density (g/cm3):      0.537
      MAX. ABS. INTENSITY / VOLUME**2:     0.9421846814    
      RIR:      0.571
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                35.25        100.00        2.5461    1   1   1         8
                40.93         48.23        2.2050    2   0   0         6
                59.27         28.64        1.5592    2   2   0        12
                70.87         29.85        1.3297    3   1   1        24
                74.54          8.27        1.2731    2   2   2         8
                88.73          3.43        1.1025    4   0   0         6
================================================================================