Andreyivanovite
      Kumar S, Krishnamurthy A, Srivastava B K, Das A, Paranjpe S K
      Pramana - Journal of Physics 63 (2004) 199-205
      Magnetization and neutron diffraction studies on FeCrP
      Locality: synthetic
      _database_code_amcsd 0015325

      CELL PARAMETERS:    5.8330   3.5690   6.6580   90.000   90.000   90.000
      SPACE GROUP: Pnma      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    138.606
      Density (g/cm3):      6.651
      MAX. ABS. INTENSITY / VOLUME**2:      50.13968276    
      RIR:      2.455
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                20.24          7.05        4.3874    1   0   1         4
                26.78          2.54        3.3290    0   0   2         2
                30.93          1.73        2.8913    1   0   2         4
                32.34         10.25        2.7686    1   1   1         8
                39.92         45.74        2.2584    2   1   0         4
                40.14        100.00        2.2466    1   1   2         8
                41.15         13.24        2.1937    2   0   2         4
                42.26         80.99        2.1387    2   1   1         8
                43.64         30.81        2.0743    1   0   3         4
                48.29         34.11        1.8847    0   1   3         4
                48.72          9.76        1.8689    2   1   2         8
                48.79         31.30        1.8664    3   0   1         4
                50.92         20.71        1.7934    1   1   3         8
                51.19         43.63        1.7845    0   2   0         2
                51.76         10.01        1.7661    2   0   3         4
                54.67         15.48        1.6789    3   0   2         4
                55.18          4.09        1.6645    0   0   4         2
                55.57          5.96        1.6539    3   1   1         8
                57.59          3.91        1.6006    1   0   4         4
                58.29          5.12        1.5829    2   1   3         8
                63.62          1.88        1.4625    3   0   3         4
                65.53          1.69        1.4245    4   0   1         4
                67.68          4.64        1.3843    2   2   2         8
                69.48         11.77        1.3528    1   2   3         8
                70.50          4.77        1.3357    4   0   2         4
                71.28          3.14        1.3230    4   1   1         8
                72.86          2.74        1.2982    1   0   5         4
                73.41         14.71        1.2898    3   2   1         8
                75.78          5.02        1.2553    2   2   3         8
                76.09          3.06        1.2510    4   1   2         8
                76.33          5.62        1.2476    0   1   5         4
                78.17          9.25        1.2228    3   2   2         8
                78.60          2.55        1.2172    0   2   4         4
                79.05          4.74        1.2113    2   0   5         4
                80.60         16.03        1.1919    3   1   4         8
                80.63          2.35        1.1915    1   2   4         8
                84.46          3.42        1.1471    2   1   5         8
                85.93          1.40        1.1311    3   2   3         8
                87.65          1.21        1.1133    4   2   1         8
                88.83          2.94        1.1015    2   3   0         4
                88.97          6.71        1.1002    1   3   2         8
                89.31          1.54        1.0969    4   0   4         4
                89.63         11.15        1.0938    5   1   1         8
================================================================================