Ba0.8 Bi0.2 F2.2
      Soubeyroux J, Reau J, Wahbi M, Senegas, Soo S
      Solid State Communications 82 (1992) 63-70
      Neutron diffraction investigation of the Ba1-xBixF2-x solid solution
      _cod_database_code 1008591
      _database_code_amcsd 0016482

      CELL PARAMETERS:    6.1118   6.1118   6.1118   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    228.301
      Density (g/cm3):      5.628
      MAX. ABS. INTENSITY / VOLUME**2:      243.4539678    
      RIR:     14.086
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                25.24        100.00        3.5286    1   1   1         8
                29.22         32.90        3.0559    2   0   0         6
                41.80         57.39        2.1608    2   2   0        12
                49.46         44.80        1.8428    3   1   1        24
                51.82          7.97        1.7643    2   2   2         8
                60.60          7.66        1.5280    4   0   0         6
                66.71         15.42        1.4021    3   3   1        24
                68.68          8.80        1.3666    4   2   0        24
                76.33         13.49        1.2476    4   2   2        24
                81.90          7.61        1.1762    5   1   1        24
                81.90          2.36        1.1762    3   3   3         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.