F2.3 Pb0.85 Th0.15
      Soubeyroux J, Reau J, Matar S, Hagenmueller P, Lucat C
      Solid State Ionics 2 (1981) 215-229
      Etude par diffraction de neutrons de la solution solide Pb1-x Thx F2+2x
      _cod_database_code 1008614
      _database_code_amcsd 0016505

      CELL PARAMETERS:    5.9581   5.9581   5.9581   90.000   90.000   90.000
      SPACE GROUP: Fm3m      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    211.506
      Density (g/cm3):      7.983
      MAX. ABS. INTENSITY / VOLUME**2:      526.4197271    
      RIR:     21.471
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                25.90        100.00        3.4399    1   1   1         8
                30.00         37.99        2.9790    2   0   0         6
                42.93         52.20        2.1065    2   2   0        12
                50.83         45.20        1.7964    3   1   1        24
                53.26          9.45        1.7200    2   2   2         8
                62.34          6.79        1.4895    4   0   0         6
                68.67         15.53        1.3669    3   3   1        24
                70.71         10.94        1.3323    4   2   0        24
                78.67         12.12        1.2162    4   2   2        24
                84.49          8.11        1.1466    5   1   1        24
                84.49          2.73        1.1466    3   3   3         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.