Labuntsovite-Mn
Golovastikov N I
Soviet Physics Crystallography 18 (1974) 596-599
Crystal structure of the alkali titanosilicate labuntsovite
Sample: half-cell
_database_code_amcsd 0015563
14.18 7.74 13.70 90 90 117. B2/m
atom     x     y     z   occ  Biso
Na   .0889 .4907 .2355 .3425 2.084
K1   .0892 .8464     0    .5 1.712
OHK1 .0892 .8464     0    .5 1.712
K2   .0807 .8025    .5 .6525 2.328
Ti1      0     0     0   .75  .935
Ti2      0     0 .2291   .95 1.065
Ti3    .25     0   .25   .98 1.025
Si1  .1806 .2506 .3889        .889
Si2  .2077 .3028 .1105        .787
O1   .0979 .8879 .2262       1.584
O2   .0815 .1718 .1188        .874
O3   .0819 .1957 .3212       1.179
O4   .2365 .1127 .3739       1.804
O5   .2331 .5246 .1287       1.516
O6   .2271 .763  .3182        .997
O7   .2456 .2836     0         1.1
O8   .1373 .2287    .5       1.149
Wat1 .0182 .5092 .1161 .4175 2.448
Wat2 .0231 .5061 .3444 .4388 2.572