Insizwaite
      Wallbaum H J
      Zeitschrift fur Metallkunde 35 (1943) 200-201
      Die kristallstrukturen von Bi2Pt und Sn2Pt
      Locality: synthetic
      _database_code_amcsd 0015828

      CELL PARAMETERS:    6.6830   6.6830   6.6830   90.000   90.000   90.000
      SPACE GROUP: Pa3       
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    298.479
      Density (g/cm3):     13.640
      MAX. ABS. INTENSITY / VOLUME**2:      535.5262815    
      RIR:     12.784
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                23.05          2.24        3.8584    1   1   1         8
                26.68         42.35        3.3415    2   0   0         6
                29.90        100.00        2.9887    2   1   0        12
                32.83         82.32        2.7283    2   1   1        24
                38.09         25.70        2.3628    2   2   0        12
                44.99         88.76        2.0150    3   1   1        24
                47.11          8.91        1.9292    2   2   2         8
                49.15         29.07        1.8535    3   0   2        12
                51.14         27.11        1.7861    3   2   1        24
                51.14         16.36        1.7861    3   1   2        24
                54.96          4.26        1.6708    4   0   0         6
                60.37          1.91        1.5332    3   3   1        24
                62.11          4.15        1.4944    4   0   2        12
                62.11          4.15        1.4944    4   2   0        12
                63.83         18.47        1.4584    4   2   1        24
                65.51          8.81        1.4248    3   3   2        24
                68.82          7.59        1.3642    4   2   2        24
                73.65          4.72        1.2861    3   3   3         8
                73.65         21.22        1.2861    5   1   1        24
                76.81         12.29        1.2410    4   2   3        24
                76.81          3.63        1.2410    5   0   2        12
                78.37          3.61        1.2201    5   2   1        24
                78.37          6.03        1.2201    5   1   2        24
                81.47         19.49        1.1814    4   4   0        12
                87.60          4.70        1.1138    4   4   2        24
                89.12          3.03        1.0987    6   1   0        12
================================================================================