Clinoferrosilite Sueno S, Kimata M, Prewitt C T American Mineralogist 69 (1984) 264-269 The crystal structure of high clinoferrosilicate T = 1050 C _database_code_amcsd 0000936 CELL PARAMETERS: 9.9280 9.1790 5.3380 90.000 110.200 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 456.527 Density (g/cm3): 3.838 MAX. ABS. INTENSITY / VOLUME**2: 16.73995849 RIR: 1.420 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.54 28.16 6.5389 1 1 0 4 19.05 35.00 4.6587 2 0 0 2 19.54 5.56 4.5437 -1 1 1 4 26.34 2.39 3.3841 0 2 1 4 27.28 34.51 3.2695 2 2 0 4 28.76 100.00 3.1038 -2 2 1 4 29.77 20.47 3.0015 -3 1 1 4 30.38 48.16 2.9419 3 1 0 4 30.76 2.55 2.9069 1 3 0 4 33.95 56.13 2.6408 -1 3 1 4 35.12 5.13 2.5550 -1 1 2 4 35.85 43.63 2.5048 0 0 2 2 36.27 25.77 2.4770 2 2 1 4 37.40 13.73 2.4044 1 3 1 4 38.65 2.81 2.3293 4 0 0 2 39.67 1.12 2.2718 -2 2 2 4 40.31 5.28 2.2373 3 1 1 4 40.96 38.74 2.2035 -3 3 1 4 41.05 2.82 2.1987 0 2 2 4 41.62 9.65 2.1700 1 1 2 4 41.63 9.41 2.1696 -4 2 1 4 42.93 20.76 2.1067 -4 0 2 2 43.37 3.47 2.0863 0 4 1 4 43.57 2.10 2.0771 4 2 0 4 43.99 1.20 2.0586 2 4 0 4 44.98 5.62 2.0152 -2 4 1 4 46.73 9.98 1.9439 2 0 2 2 48.25 1.43 1.8861 -3 3 2 4 49.48 4.57 1.8420 3 3 1 4 50.43 3.53 1.8095 2 4 1 4 50.68 11.34 1.8012 1 5 0 4 51.02 6.53 1.7900 2 2 2 4 52.64 4.50 1.7387 4 2 1 4 53.10 1.48 1.7247 -2 4 2 4 53.22 1.49 1.7210 -1 1 3 4 54.21 1.87 1.6920 0 4 2 4 55.16 20.15 1.6651 -5 3 1 4 55.38 14.48 1.6589 -2 2 3 4 55.41 4.77 1.6582 3 1 2 4 56.28 1.16 1.6347 4 4 0 4 58.03 3.94 1.5894 -3 5 1 4 58.08 5.12 1.5881 -6 0 2 2 58.39 3.25 1.5804 3 5 0 4 59.41 1.39 1.5556 -6 2 1 4 59.53 5.01 1.5529 6 0 0 2 60.52 8.17 1.5298 0 6 0 2 60.93 9.55 1.5205 -1 3 3 4 61.20 5.15 1.5146 -3 3 3 4 61.36 1.78 1.5109 -1 5 2 4 61.82 2.73 1.5008 -6 2 2 4 63.21 3.65 1.4711 4 0 2 2 63.89 4.40 1.4571 -3 5 2 4 64.06 1.03 1.4535 2 6 0 4 64.92 2.22 1.4365 3 5 1 4 65.86 1.08 1.4182 1 5 2 4 66.50 2.45 1.4061 -2 4 3 4 66.71 16.11 1.4022 5 3 1 4 67.65 4.97 1.3850 1 3 3 4 68.18 5.37 1.3755 -7 1 2 4 68.39 4.54 1.3717 -5 3 3 4 69.08 1.30 1.3597 2 2 3 4 71.58 1.54 1.3182 -3 1 4 4 71.64 1.47 1.3173 7 1 0 4 72.27 4.54 1.3073 -4 0 4 2 72.38 8.03 1.3056 0 6 2 4 74.15 1.94 1.2787 4 6 0 4 74.23 1.47 1.2775 -2 2 4 4 74.92 1.15 1.2675 -1 5 3 4 75.98 1.80 1.2524 0 0 4 2 76.75 4.19 1.2417 3 5 2 4 77.04 2.15 1.2379 -4 6 2 4 79.77 1.56 1.2022 2 6 2 4 80.13 1.38 1.1977 -6 0 4 2 82.89 1.05 1.1647 8 0 0 2 88.10 1.02 1.1088 -7 -5 2 4 88.27 3.01 1.1071 -2 8 1 4 88.81 2.13 1.1018 -6 6 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.