Vesuvianite Fitzgerald S, Rheingold A L, Leavens P B American Mineralogist 71 (1986) 1483-1488 Crystal structure of a non-P4/nnc vesuvianite from Asbestos, Quebec _database_code_amcsd 0001060 15.504 15.504 11.808 90 90 90 *P4/n .25 -.25 0 atom x y z occ Uiso U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Si1a -.25 .25 .5 .006 .006 .004 0 0 0 Si1b -.25 .25 0 .49 .006 .006 .005 0 0 0 Al1b -.25 .25 0 .51 .006 .006 .005 0 0 0 Si2a -.0399 .3180 .1308 .006 .005 .005 .001 .001 .000 Si2b -.0422 .1797 .3727 .005 .005 .006 .000 .000 .000 Si3a .0795 .1506 .6364 .007 .005 .005 -.001 .000 .000 Si3b .0889 .3482 -.1335 .009 .004 .005 -.001 .001 -.001 Ca1a -.25 .25 .2498 .011 .006 .004 -.001 0 0 Ca2a .1902 -.0421 .6215 .007 .008 .008 .000 -.001 .000 Ca2b -.0457 .1880 -.1191 .009 .006 .007 .001 .000 .000 Ca3a .1782 .4005 .1222 .011 .009 .014 -.002 -.002 .002 Ca3b .3147 .3958 -.6043 .010 .009 .013 .001 -.001 -.003 Cac1 .25 .25 -.3498 .68 .009 Cac2 .25 .25 -.1499 .26 .008 Mnc2 .25 .25 -.1499 .06 .008 Al1a -.1136 .1194 .1253 .007 .008 .008 .000 .001 .000 Al1b -.1229 .1111 .6266 .006 .005 .007 .000 .000 .000 Ala1 0 0 .5 .005 .005 .006 .001 .001 -.001 Ala2 0 .5 0 .914 .005 .005 .009 -.001 .000 .001 Mga2 0 .5 0 .186 .005 .005 .009 -.001 .000 .001 Alb1 .25 .25 -.0297 .5 .003 Alb2 .25 .25 -.4652 .5 .003 O1a -.2215 .1723 .0858 .011 .007 .006 .001 .001 .001 O1b -.2823 .1733 .4144 .008 .006 .006 -.001 .000 .001 O2a -.1187 .1574 .2808 .007 .008 .009 .000 -.002 .002 O2b -.1166 .3384 .2239 .010 .009 .005 .000 .002 .001 O3a -.0480 .2213 .0768 .010 .009 .008 .000 -.002 .000 O3b -.0496 .2772 .4240 .008 .007 .007 .000 .001 .000 O4a -.0638 .1054 .4728 .008 .006 .007 .001 -.001 .001 O4b -.0613 .3933 .0326 .011 .006 .010 .002 .004 .001 O5a -.0088 .3270 -.1757 .012 .007 .010 -.002 -.002 .001 O5b -.0190 .1677 .6795 .010 .008 .006 .001 .001 -.001 O6a .1290 .2719 -.0576 .020 .011 .011 .004 .000 .003 O6b .1135 .2293 .5624 .016 .010 .011 -.004 -.004 .005 O7a .0555 .1701 .3262 .009 .014 .006 .003 .000 -.001 O7b .0559 .3250 .1827 .006 .010 .013 -.001 .001 -.001 O8a .0929 .4381 -.0631 .008 .006 .010 .001 .000 -.002 O8b .0899 .0603 .5687 .006 .007 .012 .000 -.003 -.003 O9a .1418 .1481 .7510 .009 .011 .007 -.002 -.001 .001 O10a .25 .25 .1235 .5 .010 .010 .015 0 0 0 OH10a .25 .25 .1235 .5 .010 .010 .015 0 0 0 O10b -.25 -.25 -.3568 .5 .009 .009 .011 0 0 0 OH10b -.25 -.25 -.3568 .5 .009 .009 .011 0 0 0 OH11a -.0054 .0592 .1369 .013 .013 .007 -.004 .000 -.001 OH11b -.0640 -.0040 .6351 .013 .008 .007 .000 .002 .001