Spinel Peterson R C, Lager G A, Hitterman R L American Mineralogist 76 (1991) 1455-1458 A time-of-flight neutron powder diffraction study of MgAl2O4 at temperatures up to 1273 K sample W, T = 973 K _database_code_amcsd 0001402 CELL PARAMETERS: 8.1322 8.1322 8.1322 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 537.802 Density (g/cm3): 3.514 MAX. ABS. INTENSITY / VOLUME**2: 17.59860270 RIR: 1.631 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.90 31.36 4.6951 1 1 1 8 31.11 33.90 2.8752 2 2 0 12 36.65 100.00 2.4519 3 1 1 24 38.34 1.45 2.3476 2 2 2 8 44.57 55.27 2.0330 4 0 0 6 55.34 9.10 1.6600 4 2 2 24 59.02 2.93 1.5650 3 3 3 8 59.02 39.88 1.5650 5 1 1 24 64.86 66.12 1.4376 4 4 0 12 68.23 2.45 1.3746 5 3 1 48 73.68 2.73 1.2858 6 2 0 24 76.87 8.64 1.2401 5 3 3 24 82.11 5.54 1.1738 4 4 4 8 85.22 2.08 1.1387 5 5 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.