Spinel Peterson R C, Lager G A, Hitterman R L American Mineralogist 76 (1991) 1455-1458 A time-of-flight neutron powder diffraction study of MgAl2O4 at temperatures up to 1273 K sample UC, T = 1273 K _database_code_amcsd 0001411 CELL PARAMETERS: 8.1509 8.1509 8.1509 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 541.523 Density (g/cm3): 3.489 MAX. ABS. INTENSITY / VOLUME**2: 17.18672505 RIR: 1.604 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.86 29.67 4.7059 1 1 1 8 31.03 34.17 2.8818 2 2 0 12 36.56 100.00 2.4576 3 1 1 24 38.25 1.55 2.3530 2 2 2 8 44.46 53.71 2.0377 4 0 0 6 55.21 9.17 1.6638 4 2 2 24 58.87 2.97 1.5686 3 3 3 8 58.87 37.84 1.5686 5 1 1 24 64.69 63.07 1.4409 4 4 0 12 68.05 2.00 1.3778 5 3 1 48 73.48 2.76 1.2888 6 2 0 24 76.66 8.08 1.2430 5 3 3 24 81.88 4.87 1.1765 4 4 4 8 84.98 1.66 1.1414 5 5 1 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.