Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 300 K _database_code_amcsd 0002576 CELL PARAMETERS: 8.4418 8.4418 8.4418 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 601.596 Density (g/cm3): 5.318 MAX. ABS. INTENSITY / VOLUME**2: 104.3202217 RIR: 6.387 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.20 4.60 4.8739 1 1 1 8 29.94 36.06 2.9846 2 2 0 12 35.26 100.00 2.5453 3 1 1 24 36.88 7.28 2.4369 2 2 2 8 42.85 13.29 2.1105 4 0 0 6 53.15 12.59 1.7232 4 2 2 24 56.66 28.77 1.6246 5 1 1 24 56.66 5.68 1.6246 3 3 3 8 62.21 39.84 1.4923 4 4 0 12 70.56 4.68 1.3348 6 2 0 24 73.57 9.20 1.2874 5 3 3 24 74.57 3.46 1.2726 6 2 2 24 78.50 1.41 1.2185 4 4 4 8 86.22 5.79 1.1281 6 4 2 48 89.09 6.21 1.0990 5 5 3 24 89.09 8.25 1.0990 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.