Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 500 K _database_code_amcsd 0002577 CELL PARAMETERS: 8.4560 8.4560 8.4560 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 604.637 Density (g/cm3): 5.291 MAX. ABS. INTENSITY / VOLUME**2: 101.7005372 RIR: 6.259 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.17 4.66 4.8821 1 1 1 8 29.89 36.11 2.9896 2 2 0 12 35.20 100.00 2.5496 3 1 1 24 36.82 7.33 2.4410 2 2 2 8 42.77 13.28 2.1140 4 0 0 6 53.06 12.21 1.7261 4 2 2 24 56.55 27.88 1.6274 5 1 1 24 56.55 5.54 1.6274 3 3 3 8 62.09 38.37 1.4948 4 4 0 12 70.42 4.39 1.3370 6 2 0 24 73.43 8.68 1.2895 5 3 3 24 74.42 3.33 1.2748 6 2 2 24 78.34 1.36 1.2205 4 4 4 8 86.04 5.23 1.1300 6 4 2 48 88.90 7.57 1.1009 7 3 1 48 88.90 5.66 1.1009 5 5 3 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.