Franklinite Pavese A, Levy D, Hoser A American Mineralogist 85 (2000) 1497-1502 Cation distribution in synthetic zinc ferrite (Zn0.97Fe2.02O4) from in situ high temperature neutron powder diffraction Sample at T = 700 K _database_code_amcsd 0002578 CELL PARAMETERS: 8.4713 8.4713 8.4713 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 607.925 Density (g/cm3): 5.263 MAX. ABS. INTENSITY / VOLUME**2: 99.27120674 RIR: 6.142 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.14 4.69 4.8909 1 1 1 8 29.83 36.21 2.9951 2 2 0 12 35.13 100.00 2.5542 3 1 1 24 36.75 7.31 2.4455 2 2 2 8 42.69 13.27 2.1178 4 0 0 6 52.95 11.88 1.7292 4 2 2 24 56.44 27.09 1.6303 5 1 1 24 56.44 5.40 1.6303 3 3 3 8 61.97 37.11 1.4975 4 4 0 12 70.28 4.14 1.3394 6 2 0 24 73.28 8.21 1.2919 5 3 3 24 74.26 3.16 1.2771 6 2 2 24 78.17 1.31 1.2227 4 4 4 8 85.85 4.76 1.1320 6 4 2 48 88.70 5.19 1.1029 5 5 3 24 88.70 6.94 1.1029 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.